polyamide
6 with
30 % mineral
flame-retardant
(PA 6 M30 V0)
We use this material in the following process(es):
Injection moulding.
Injection moulded parts up to 16.000 g
|
|
| Material number
|
|
1119 |
|
| Density
|
ISO 1183 |
1,56 |
g/cm3 |
| Condition of the test specimen
|
|
dry
|
|
| |
|
Mechanical properties
|
| Tensile strength
|
ISO 527 |
70/40 |
MPa |
| Elongation at break
|
ISO 527 |
2,5/4 |
% |
| Tensile modulus
|
ISO 527 |
8000/3500 |
MPa |
| Ball pressure hardness
|
ISO 2039-1 |
200 |
MPa |
| Standard for ball pressure hardness
|
|
H358/30 |
|
| Hardness Shore (A/D) or Rockwell (R/L/M)
|
ISO 868, ISO 2039-2 |
D82 |
- |
| Izod notched impact strength at 23 °C
|
ISO 180/1A |
3 |
KJ/m2 |
| Charpy notched impact strength at 23 °C
|
ISO 179/1eA |
5/5 |
KJ/m2 |
| |
|
Electrical properties
|
| Dielectric constant at 50 Hz
|
IEC 60250 |
3,6/10 |
- |
| Dielectric constant at 1 MHz
|
IEC 60250 |
3,2/3,7 |
- |
| Dissipation factor at 50 Hz
|
IEC 60250 |
85/3000 |
1E-4 |
| Dissipation factor at 1 MHz
|
IEC 60250 |
140/900 |
1E-4 |
| Dielectric strength
|
IEC 60243-1 |
25 |
kV/mm |
| Thickness for electric strength
|
|
1,0 |
mm |
| Volume resistivity
|
IEC 60093 |
1012/1010 |
Ohm · m |
| Surface resistivity
|
IEC 60093 |
1014/1013 |
Ohm |
| Comparative tracking index
|
IEC 60112 |
375 |
- |
| |
|
Thermal properties
|
| Thermal conductance
|
DIN 52 612 |
0,21 |
W/K m |
| Linear thermal expansion along|cross to direction of flow
|
ISO 11359 |
50 |
10-6/K |
| Melting point or glass transition temp.
|
ISO 11357 |
220 |
°C |
| Heat distortion temperature A
|
ISO 75 HDT/A (1.8 MPa) |
145 |
°C |
| Heat distortion temperature B
|
ISO 75 HDT/B (0,45 MPa) |
205 |
°C |
| Short time use temperature
|
|
180 |
°C |
| Continuous use temperature
|
|
140 5) |
°C |
| Minimal use temperature
|
|
-40 |
°C |
| |
|
Other properties
|
| Humidity absorption at 23°C/50%
|
ISO 62 |
1,7 |
% |
| Water absorption
|
ISO 62 |
6,2 |
% |
| Flammability UL 94
|
IEC 60695-11-10 |
V-0 |
- |
| Thickness for UL 94
|
|
3,0 |
mm |
| Transparency (opaque/translucent/clear)
|
|
opaque |
|
| Raw material
|
|
Akulon K223-KMV6 (DSM) |
|
| |
|
|
5) : Thermal ageing UL 746 (RTI) Mechanical W/O Imp., 40 000 h
This datasheet is a print-out of the material database
RIWETA 4.1 and is intended for
personal use only.
The figures in this datasheet are guide values. The
values are affected by processing conditions, modifications, additives and environmental conditions
and they do not release you from the obligation to
check the validity and to undertake tests on your
own. The information given is based on our state of
knowledge. The material data is not to be construed
as guaranteeing specific properties and the data can
not be used to deduce the suitability for a particular
application.
It remains the responsibility of the user of our products
not to infringe patent rights and to comply with existing
laws and regulations.
Hüttig GmbH
Technische Kunststoffteile
Industriegebiet
D-07774 Dornburg-Camburg
|
Home
Service
PA 6 M30 V0